http://dspace.bsu.edu.ru/handle/123456789/4522| Title: | Dynamic recrystallization and grain growth in a ZK60 magnesium alloy sheet produced by isothermal rolling |
| Authors: | Galiyev, A. Kaibyshev, R. |
| Keywords: | technique metal science magnesium alloy dynamic recrystallization grain refinement ultrafine-grained structure |
| Issue Date: | 2004 |
| Citation: | Galiyev, A. Dynamic recrystallization and grain growth in a ZK60 magnesium alloy sheet produced by isothermal rolling / A. Galiyev, R. Kaibyshev // Materials Science Forum. - 2004. - Vol.467-470, N2.-P. 1175-1180. - Refer.: p. 1180. |
| Abstract: | A ZK60 magnesium alloy was subjected to isothermal rolling (IR) at 275 and 300°C. This processing resulted in grain refinement through dynamic recrystallization (DRX) at both temperatures. The recrystallized volume fractions of 82 and 95% and average sizes of fine grains of 2,5 and 3,7 μm were achieved after IR at 275 and 300°C, respectively. It was shown that the ultrafine-grained structure produced by DRX at 300°C exhibited higher stability under following static and dynamic annealing than that produced at 275°C |
| URI: | http://dspace.bsu.edu.ru/handle/123456789/4522 |
| Appears in Collections: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| File | Description | Size | Format | |
|---|---|---|---|---|
| Galiyev A._Dynamic.pdf | 573.58 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.