Название: | Effect of long-term creep on microstructure of a 9% Cr heat resistant steel |
Авторы: | Dudko, V. Fedoseeva, A. Kozlov, P. Skorobogatykh, V. Shchenkova, I. Kaibyshev, R. |
Ключевые слова: | technique metal science high-chromium heat resistant steel martensite tempering carbides mechanical properties |
Дата публикации: | 2014 |
Библиографическое описание: | Effect of long-term creep on microstructure of a 9% Cr heat resistant steel / V. Dudko [et al.] // Materials Science Forum. - 2014. - Vol.783-786.-P. 1839-1844. |
Краткий осмотр (реферат): | The effect of long-term creep at 600°C under 137 MPa on the microstructure of a P92- type steel was investigated. The microstructure after tempering consisted of laths with an average thickness of 400 nm. Dispersion of secondary phases consists of M₂₃C₆ carbides with an average size of 85 nm located mainly on lath, block and prior austenite boundaries and MX carbonitrides with average size of 31 nm homogeniously distributed throughout |
URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/20251 |
Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
Dudko_Effect_2013.pdf | 706.65 kB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.