http://dspace.bsu.edu.ru/handle/123456789/4739| Название: | Microstructure evolution in a 3%Co modified P911 heat resistant steel under tempering and creep conditions |
| Авторы: | Kaibyshev, R. Belyakov, A. Schenkova, I. Molodov, D. |
| Ключевые слова: | metal technology steel production steel heat resistant steel tempered martensite creep grain / subgrain growth dispersed particles pinning pressure |
| Дата публикации: | 2011 |
| Библиографическое описание: | Microstructure evolution in a 3%Co modified P911 heat resistant steel under tempering and creep conditions / A. Kipelova, R. Kaibyshev, A. Belyakov, et al. ; Belgorod State University // Materials science and engineering A. - 2011. - Vol.528.-P. 1280-1286. - doi: 10.1016/j.msea.2010.10.006. |
| Краткий осмотр (реферат): | Microstructure evolution was studied in a 3%Co modified P911 heat resistant steel during creep tests at 873 and 923K to failure, which occurred in 4103 and 4743h, respectively. The tempered marten site lath structure consisted of packets, blocks and laths |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/4739 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Kipelova et al_Microstructure evolution.pdf | 1.12 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.