http://dspace.bsu.edu.ru/handle/123456789/51487| Название: | Precipitation and flow behavior of AISI 630 stainless steel deformed at elevated temperatures |
| Авторы: | Sangarimotlagh, Z. Tolaminejad, B. Momeni, A. Fedorova, I. Zuiko, I. Kaibyshev, R. |
| Ключевые слова: | technique metal science AISI 630 constitutive analysis dynamic precipitation dynamic recrystallization hot deformation stress relaxation |
| Дата публикации: | 2022 |
| Библиографическое описание: | Precipitation and flow behavior of AISI 630 stainless steel deformed at elevated temperatures / Z. Sangarimotlagh [et al.] // Journal of Materials Engineering and Performance. - 2022. - 14 September. - URL: https://link.springer.com/content/pdf/10.1007/s11665-022-07340-z.pdf?pdf=button |
| Краткий осмотр (реферат): | Hot compression tests were performed on the samples of AISI 630 stainless steel in the temperature range of 900-1050 C and at strain rates of 10–3- 1 s21. Single peak stress flow behavior was observed at all deformation conditions. An irregular relationship was found between the peak point of flow curves and processing condition, i.e., temperature and strain rate. The stress relaxation tests at the temperature range of 900-1050 C revealed that dynamic precipitation (DP) of carbides in the matrix and grain boundaries causes the considered irregularities in the peak stress |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/51487 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Sangarimotlagh_Precipitati.pdf | 3.46 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.