http://dspace.bsu.edu.ru/handle/123456789/64101| Название: | The Effect of Prolonged Annealing on the Structural Stability of Nanoparticle-Hardened Low-Carbon 9% Cr-3% Co Steel |
| Авторы: | Fedoseeva, A. E. Degtyareva, S. I. |
| Ключевые слова: | technique metal science steels martensitic high-temperature stee heat treatment prolonged annealing microstructure secondary phase particles softening |
| Дата публикации: | 2022 |
| Библиографическое описание: | Fedoseeva, A.E. The Effect of Prolonged Annealing on the Structural Stability of Nanoparticle-Hardened Low-Carbon 9% Cr-3% Co Steel / A.E. Fedoseeva, S.I. Degtyareva // Physics of Metals and Metallography. - 2022. - Vol.123, №10.- P. 1041-1047. - Doi: 10.1134/S0031918X22600889. - Refer.: p. 1046-1047. |
| Краткий осмотр (реферат): | The effect of long-term annealing on the structure of low-carbon 9% Cr-3% Co steel hardened with nanoparticles has been studied. Annealing was performed for 100, 500, 1000, and 3000 hours at a temperature of 650°C |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/64101 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |