http://dspace.bsuedu.ru/handle/123456789/65342| Название: | Morphology of secondary phase particles and stability of subgrain structure in martensitic steel 10Cr9Co3W2MoVNbB (ASTM A335 P92) under creep conditions |
| Авторы: | Tkachev, E.S. Kaibyshev, R.O. |
| Ключевые слова: | technique metal science high-chromium martensitic steel creep subgrain structure coarsening of precipitates |
| Дата публикации: | 2024 |
| Библиографическое описание: | Tkachev E.S. Morphology of secondary phase particles and stability of subgrain structure in martensitic steel 10Cr9Co3W2MoVNbB (ASTM A335 P92) under creep conditions / E.S. Tkachev, R.O. Kaibyshev // Metal Science and Heat Treatment. - 2024. - Vol.66, №7-8.-P. 474-481. - Doi: 10.1007/s11041-024-01073 -7. - Refer.: p. 480-481. |
| Краткий осмотр (реферат): | The creep behavior of high-chromium martensitic steel 10Cr9Co3W2MoVNbB (ASTM A335 P92) at a temperature of 650°C and stresses 100-180 MPa is studied. The effect of creep on the subgrain structure and the characteristics of secondary particles are determined using transmission electron microscopy |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsuedu.ru/handle/123456789/65342 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |