http://dspace.bsu.edu.ru/handle/123456789/42670| Название: | The effect of Gd addition on the kinetics of α₂→γ transformation in γ-TiAl based alloys |
| Авторы: | Sokolovsky, V. S. Stepanov, N. D. Zherebtsov, S. V. Volokitina, E. I. Salishchev, G. A. |
| Ключевые слова: | technique metal science alloys microalloying nucleation and growth phase transformation microstructure segregation |
| Дата публикации: | 2020 |
| Библиографическое описание: | The effect of Gd addition on the kinetics of α₂→γ transformation in γ-TiAl based alloys / V.S. Sokolovsky [et al.] // Intermetallics. - 2020. - Vol.120.-Art. 106759. - Doi: 10.1016/j.intermet.2020.106759. |
| Краткий осмотр (реферат): | The effect of Gd on the formation of a lamellar structure during ageing of quenched γ-TiAl studied. Ti-47.1Al-1.8Nb-0.5Zr-0.3V-0.001Gd (0.001Gd) and Ti-46.9Al-1.6Nb-0.5Zr-0.5V-0.03Gd (0.03Gd) alloys were quenched from the alpha-phase field and aged at 400–800 °C. After quenching, a small amount of Gd₂TiO₅ particles was found in both alloysbased alloys was |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/42670 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Sokolovsky_The effect.pdf | 3.52 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.