Features in low-temperature electrical resistivity of amorphous Cd₃As₂ films due to hopping conductivity with changing activation energy

Abstract

Amorphous Cd₃As₂ films were deposited on single-crystalline SrTiO3 substrate by high-frequency non-reactive magnetron sputtering. Electrical resistivity of the film, measured within 3-75 K range, increases at cooling. Below ~70 K, negative transverse magnetoresistance observed. Features in electrical resistivity and magnertoresistance can be attributed to variable-range hopping conductivity of the Mott type with local activation energy, which is temperature-dependent. Two temperature ranges in the hopping conductivity observed